1 This specification is under the jurisdiction of ASTM Committee A01 on Steel, 2 For referenced ASTM standards, visit the ASTM website, , or. ASTM Aa(). Standard Specification for Tool Steel High Speed. standard by ASTM International, 03/01/ View all product details. Most Recent. ASTM A Standard Specification for High Speed Tool Steel.

Author: Arashijar Nikojind
Country: Morocco
Language: English (Spanish)
Genre: Career
Published (Last): 1 May 2006
Pages: 402
PDF File Size: 5.98 Mb
ePub File Size: 18.58 Mb
ISBN: 720-9-14972-424-6
Downloads: 7618
Price: Free* [*Free Regsitration Required]
Uploader: Shakazuru

Grades and Trade Names

ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date. Do Not forge below F. Forge at F down to F.

Preheat at F before heating for hardening. Hardens by heat treatment and quenching. Unless otherwise specified, material shall be made by an electric melting process.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. Anneal at F and slow furnace cool at 40 F per hour, or less. Selection will depend upon design, service conditions, and mechanical properties. See “Forging” and consult the supplier for information on working at lower temperatures.

  MALAGUENA LECUONA GUITAR PDF

Primarily used for cutting tools. Then heat rapidly from F to F and hold for 3 to 5 minutes followed by quenching in oil, air or salt bath.

See “Heat Treatment” and “Tempering”. Not applicable to this alloy.

Temper at F for a hardness of Rockwell C 60 to It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.

Formed by machining or forging and then machining. It may be shaped by grinding but is relatively poor in regard to capability of being ground.

ASTM A600, Tool Steel High Speed

Link to Active This link will always route to the current Active version of the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. M2 is classified as a “medium” machinability tool steel in the annealed condition. Adtm will offer small quantity buys while mills will generally only sell large quantities, with delivery times anywhere from 10 to 50 weeks depending on size and form required This material is stocked primarily in Bar Products by 28 distributors but is also available to a lesser extent in Flat Rolled Products, Wire Products, and Shapes.

  LIBRO DE BERTHA HIGASHIDA CIENCIAS DE LA SALUD PDF

Two intermediate high speed tool steels designated as M50 and M52 are also covered.

A chemical analysis of each heat of steel shall be made to determine the percentage of awtm elements specified including carbon, manganese, phosphorus, sulfur, silicon, chromium, vanadium, tungsten, molybdenum, and cobalt and these values shall conform to the requirements as to the prescribed chemical composition.

Cold working may be accomplished with the alloy in the annealed condition. Modulus of Elasticity Tension. The M2 alloy has somewhat better wear resistance than M1.

Consult the alloy supplier for information on the advisability of welding. The a00 Brinell hardness and minimum Rockwell C hardness for the tool steels are given. Historical Version s – view previous versions of standard.

This abstract is a brief summary of the referenced standard.